陶氏杜邦PA66 45HSB是一种高粘度聚酰胺66，注塑成型和挤压，性能是热稳定，颜色是NC010。
| PA66(尼龙66)45HSB/陶氏杜邦物性表参数PDF文档下载 |
原材料生产商：DuPont（陶氏杜邦）
以下是PA66(尼龙66)45HSB/陶氏杜邦/物性表参数
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.14 g/cc | 1.14 g/cc | DAM; ASTM D792 |
| 密度 | 1.14 g/cc | 0.0412 lb/in³ | DAM; ISO 1183 |
| 线性成型收缩率,Flow | 0.014 cm/cm @Thickness 2.00 mm | 0.014 in/in @Thickness 0.0787 in | DAM; ISO 294-4 |
| 线性成型收缩率，横向 | 0.014 cm/cm @Thickness 2.00 mm | 0.014 in/in @Thickness 0.0787 in | DAM; ISO 294-4 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度 | 83.0 MPa @Temperature 23.0 °C | 12000 psi @Temperature 73.4 °F | DAM; ASTM D638 |
| 抗张强度(屈服) | 55.0 MPa @Temperature 23.0 °C | 7980 psi @Temperature 73.4 °F | 50%RH; ISO 527 |
| 83.0 MPa @Temperature 23.0 °C | 12000 psi @Temperature 73.4 °F | DAM; ISO 527 | |
| 伸长率 (断裂) | >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | DAM; nominal; ISO 527 |
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |
| 90 % @Temperature 23.0 °C | 90 % @Temperature 73.4 °F | DAM; ASTM D638 | |
| Elongation at Yield | 4.0 % @Temperature 23.0 °C | 4.0 % @Temperature 73.4 °F | DAM; ISO 527 |
| 25 % @Temperature 23.0 °C | 25 % @Temperature 73.4 °F | 50%RH; ISO 527 | |
| 拉伸模量 | 1.30 GPa @Temperature 23.0 °C | 189 ksi @Temperature 73.4 °F | 50%RH; ISO 527 |
| 3.10 GPa @Temperature 23.0 °C | 450 ksi @Temperature 73.4 °F | DAM; ISO 527 | |
| 弯曲模量 | 2.80 GPa @Temperature 23.0 °C | 406 ksi @Temperature 73.4 °F | DAM; ISO 178 |
| 3.03 GPa @Temperature 23.0 °C | 439 ksi @Temperature 73.4 °F | DAM; ASTM D790 | |
| 悬壁梁缺口冲击强度 | 0.640 J/cm @Temperature 23.0 °C | 1.20 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 |
| 6.00 kJ/m² @Temperature -40.0 °C | 2.86 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 180/1A | |
| 6.00 kJ/m² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |
| 简支梁缺口冲击强度 | 0.550 J/cm² @Temperature -30.0 °C | 2.62 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA |
| 0.600 J/cm² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| Comparative Tracking Index | 600 V @Temperature 23.0 °C | 600 V @Temperature 73.4 °F | DAM; UL 746A |
| >= 600 V @Temperature 23.0 °C | >= 600 V @Temperature 73.4 °F | DAM; UL 746A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 |
| 线性热膨胀系数,横向流动 | 100 µm/m-°C @Temperature 23.0 - 55.0 °C | 55.6 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 |
| 熔融温度 | 262 °C | 504 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| 262 °C | 504 °F | DAM; ASTM D3418 | |
| 载荷下热变形温度(0.46 MPa) | 200 °C | 392 °F | DAM; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | 65.0 °C | 149 °F | DAM; ASTM D648 |
| 70.0 °C | 158 °F | DAM; ISO 75-1/-2 | |
| UL RTI | 140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | DAM; UL 746B |
| 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | DAM; UL 746B | |
| 140 °C @Thickness 0.710 mm | 284 °F @Thickness 0.0280 in | DAM; UL 746B | |
| UL RTI，机械冲击 | 95.0 °C @Thickness 0.710 mm | 203 °F @Thickness 0.0280 in | DAM; UL 746B |
| 110 °C @Thickness 1.50 mm | 230 °F @Thickness 0.0591 in | DAM; UL 746B | |
| 110 °C @Thickness 3.00 mm | 230 °F @Thickness 0.118 in | DAM; UL 746B | |
| UL RTI，机械无冲击 | 115 °C @Thickness 0.710 mm | 239 °F @Thickness 0.0280 in | DAM; UL 746B |
| 125 °C @Thickness 1.50 mm | 257 °F @Thickness 0.0591 in | DAM; UL 746B | |
| 125 °C @Thickness 3.00 mm | 257 °F @Thickness 0.118 in | DAM; UL 746B | |
| 可燃性(UL94) | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 |
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |
| HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | DAM; IEC 60695-11-10 | |
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |
| HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | DAM; UL94 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 280 - 290 °C | 536 - 554 °F | DAM; Extrusion |
| 285 °C | 545 °F | DAM; Optimum; Extrusion | |
| 290 °C | 554 °F | DAM; Optimum; Injection Molding | |
| 280 - 300 °C | 536 - 572 °F | DAM; Injection Molding | |
| 模具温度 | 70.0 °C | 158 °F | DAM; optimum; Injection Molding |
| 50.0 - 90.0 °C | 122 - 194 °F | DAM; Injection Molding | |
| 干燥温度 | 80.0 °C | 176 °F | DAM; Extrusion |
| 80.0 °C | 176 °F | DAM; Injection Molding | |
| 干燥时间 | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Injection Molding |
| 4.00 - 6.00 hour | 4.00 - 6.00 hour | DAM; Extrusion | |
| 水分含量 | <= 0.050 % | <= 0.050 % | DAM; Extrusion |
| <= 0.050 % | <= 0.050 % | DAM; Injection Molding |
| 材料描述 | 测试方法 | |
|---|---|---|
| 添加剂 | Heat Stabilizer | DAM |
| 外观 | Natural Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| Extrudable - Coating | Yes | DAM |
| Extrudable - Filament | Yes | DAM |
| Extrudable - Sheet | Yes | DAM |
| Extrudable - Tubing | Yes | DAM |
| 特性 | Heat Aging Resistance, Good | DAM |
| Molecular Wt., High | DAM | |
| Viscosity, High | DAM | |
| 形式 | Pellets | DAM |
| Generic | Nylon 66 | DAM |
| Heat Stabilized | Yes | DAM |
| Material Status | Current | DAM |
| 部件标识代码 | >PA66< | ISO 11469; DAM |
| Polymer Family | Polyamide | DAM |
| Polymer Type | PA66 | DAM |
| 加工方法 | Extrusion | DAM |
| Extrusion | DAM | |
| Injection Molding | DAM | |
| 产品分类 | Extrusion Resins | DAM |
| Unreinforced Resins | DAM | |
| 树脂识别 | PA66 | ISO 1043; DAM |
| 符合RoHS指令 | Contact Manufacturer | DAM |
| Ultrasonic Weldable | Yes | DAM |
| 用途 | Gears | DAM |
| Stock Material for Machining | DAM |
温馨提示：本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.
友情提示:
您还可以进入塑料型号栏目，查询PA66 45HSB的塑料规格
您还可以进入工程塑料栏目，查询PA66 45HSB的塑料供应商
您还可以进入塑料价格栏目，查询PA66 45HSB的价格
您还可以进入常见问题栏目，查询PA66 45HSB的物性表参数。
本文链接：http://www.xihao.site/showinfo-12-40397.htmlPA66(尼龙66)45HSB/陶氏杜邦/物性表参数