美国杜邦 73M40|美国杜邦 PA6 73M40| Zytel® 73M40价格
美国杜邦 PA6 73M40最新价格表
您也可以致电18621317168(微信同号)获取优惠报价
DuPont Performance Polymers Minlon® 73M40
Polymer,Thermoplastic,Nylon,Nylon 6,Nylon 6, 40% Mineral Filled
DuPont Performance Polymers
产品说明:
40% Mineral Reinforced Polyamide 6
Minlon 73M40 NC010 is a 40% mineral reinforced heat stabilized polyamide 6 resin for injection molding. It has isotropic properties and low warpage.
Information provided by DuPont Performance Polymers
DuPont Performance Polymers Minlon® 73M40 NC010 Nylon 6 (Unverified Data**) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.28 g/cc | 0.0462 lb/in³ | |
| 1.45 g/cc | 0.0524 lb/in³ | DAM; ISO 1183 | |
| 吸水率 | 5.4 % @Thickness 2.00 mm | 5.4 % @Thickness 0.0787 in | DAM; Sim. to ISO 62 |
| 水分吸收 | 1.80 % @Thickness 2.00 mm | 1.80 % @Thickness 0.0787 in | DAM; Sim. to ISO 62 |
| 粘度 | 105300 cP @Shear Rate 5000 1/s, Temperature 280 °C | 105300 cP @Shear Rate 5000 1/s, Temperature 536 °F | ISO 11403-1 -2 |
| 117100 cP @Shear Rate 5000 1/s, Temperature 270 °C | 117100 cP @Shear Rate 5000 1/s, Temperature 518 °F | ISO 11403-1 -2 | |
| 130500 cP @Shear Rate 5000 1/s, Temperature 260 °C | 130500 cP @Shear Rate 5000 1/s, Temperature 500 °F | ISO 11403-1 -2 | |
| 326200 cP @Shear Rate 500 1/s, Temperature 280 °C | 326200 cP @Shear Rate 500 1/s, Temperature 536 °F | ISO 11403-1 -2 | |
| 404600 cP @Shear Rate 500 1/s, Temperature 270 °C | 404600 cP @Shear Rate 500 1/s, Temperature 518 °F | ISO 11403-1 -2 | |
| 500200 cP @Shear Rate 500 1/s, Temperature 260 °C | 500200 cP @Shear Rate 500 1/s, Temperature 500 °F | ISO 11403-1 -2 | |
| 粘度测试 | 145 cm³/g | 145 cm³/g | DAM; ISO 307 1157 1628 |
| 线性成型收缩率,Flow | 0.0080 cm/cm | 0.0080 in/in | DAM; ISO 294-4 2577 |
| 线性成型收缩率，横向 | 0.0080 cm/cm | 0.0080 in/in | DAM; ISO 294-4 2577 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 59.0 MPa | 8560 psi | 50%RH; ISO 527-1/-2 |
| 87.0 MPa | 12600 psi | DAM; ISO 527-1/-2 | |
| 抗张强度 | 7.55 MPa @Strain 0.600 %, Temperature 90.0 °C | 1100 psi @Strain 0.600 %, Temperature 194 °F | DAM; ISO 11403-1 -2 |
| 8.62 MPa @Strain 1.25 %, Temperature 150 °C | 1250 psi @Strain 1.25 %, Temperature 302 °F | DAM; ISO 11403-1 -2 | |
| 8.99 MPa @Strain 0.870 %, Temperature 90.0 °C | 1300 psi @Strain 0.870 %, Temperature 194 °F | 50%RH; ISO 11403-1 -2 | |
| 20.73 MPa @Strain 0.960 %, Temperature 23.0 °C | 3007 psi @Strain 0.960 %, Temperature 73.4 °F | 50%RH; ISO 11403-1 -2 | |
| 23.1 MPa @Strain 8.78 %, Temperature 150 °C | 3350 psi @Strain 8.78 %, Temperature 302 °F | DAM; ISO 11403-1 -2 | |
| 24.23 MPa @Strain 3.51 %, Temperature 90.0 °C | 3514 psi @Strain 3.51 %, Temperature 194 °F | 50%RH; ISO 11403-1 -2 | |
| 27.06 MPa @Strain 17.23 %, Temperature 150 °C | 3925 psi @Strain 17.23 %, Temperature 302 °F | DAM; ISO 11403-1 -2 | |
| 29.08 MPa @Strain 26.18 %, Temperature 150 °C | 4218 psi @Strain 26.18 %, Temperature 302 °F | DAM; ISO 11403-1 -2 | |
| 30.54 MPa @Strain 6.08 %, Temperature 90.0 °C | 4429 psi @Strain 6.08 %, Temperature 194 °F | 50%RH; ISO 11403-1 -2 | |
| 32.34 MPa @Strain 6.02 %, Temperature 90.0 °C | 4691 psi @Strain 6.02 %, Temperature 194 °F | DAM; ISO 11403-1 -2 | |
| 33.59 MPa @Strain 8.65 %, Temperature 90.0 °C | 4872 psi @Strain 8.65 %, Temperature 194 °F | 50%RH; ISO 11403-1 -2 | |
| 39.29 MPa @Strain 12.38 %, Temperature 90.0 °C | 5699 psi @Strain 12.38 %, Temperature 194 °F | DAM; ISO 11403-1 -2 | |
| 40.94 MPa @Strain 0.800 %, Temperature 40.0 °C | 5938 psi @Strain 0.800 %, Temperature 104 °F | DAM; ISO 11403-1 -2 | |
| 42.34 MPa @Strain 19.17 %, Temperature 90.0 °C | 6141 psi @Strain 19.17 %, Temperature 194 °F | DAM; ISO 11403-1 -2 | |
| 42.45 MPa @Strain 3.81 %, Temperature 23.0 °C | 6157 psi @Strain 3.81 %, Temperature 73.4 °F | 50%RH; ISO 11403-1 -2 | |
| 50.59 MPa @Strain 0.720 %, Temperature -40.0 °C | 7337 psi @Strain 0.720 %, Temperature -40.0 °F | 50%RH; ISO 11403-1 -2 | |
| 52.12 MPa @Strain 6.65 %, Temperature 23.0 °C | 7559 psi @Strain 6.65 %, Temperature 73.4 °F | 50%RH; ISO 11403-1 -2 | |
| 56.95 MPa @Strain 9.50 %, Temperature 23.0 °C | 8260 psi @Strain 9.50 %, Temperature 73.4 °F | 50%RH; ISO 11403-1 -2 | |
| 61.67 MPa @Strain 18.04 %, Temperature 23.0 °C | 8944 psi @Strain 18.04 %, Temperature 73.4 °F | 50%RH; ISO 11403-1 -2 | |
| 66.28 MPa @Strain 2.93 %, Temperature 40.0 °C | 9613 psi @Strain 2.93 %, Temperature 104 °F | DAM; ISO 11403-1 -2 | |
| 68.33 MPa @Strain 6.04 %, Temperature 40.0 °C | 9910 psi @Strain 6.04 %, Temperature 104 °F | DAM; ISO 11403-1 -2 | |
| 70.17 MPa @Strain 9.22 %, Temperature 40.0 °C | 10180 psi @Strain 9.22 %, Temperature 104 °F | DAM; ISO 11403-1 -2 | |
| 73.04 MPa @Strain 1.41 %, Temperature 23.0 °C | 10590 psi @Strain 1.41 %, Temperature 73.4 °F | DAM; ISO 11403-1 -2 | |
| 76.08 MPa @Strain 1.16 %, Temperature -40.0 °C | 11030 psi @Strain 1.16 %, Temperature -40.0 °F | 50%RH; ISO 11403-1 -2 | |
| 92.16 MPa @Strain 2.56 %, Temperature 23.0 °C | 13370 psi @Strain 2.56 %, Temperature 73.4 °F | DAM; ISO 11403-1 -2 | |
| 93.81 MPa @Strain 1.80 %, Temperature 0.000 °C | 13610 psi @Strain 1.80 %, Temperature 32.0 °F | DAM; ISO 11403-1 -2 | |
| 95.68 MPa @Strain 1.60 %, Temperature -40.0 °C | 13880 psi @Strain 1.60 %, Temperature -40.0 °F | 50%RH; ISO 11403-1 -2 | |
| 108 MPa @Strain 2.00 %, Temperature -40.0 °C | 15700 psi @Strain 2.00 %, Temperature -40.0 °F | DAM; ISO 11403-1 -2 | |
| 108.25 MPa @Strain 2.89 %, Temperature 0.000 °C | 15700 psi @Strain 2.89 %, Temperature 32.0 °F | DAM; ISO 11403-1 -2 | |
| 108.64 MPa @Strain 2.02 %, Temperature -40.0 °C | 15757 psi @Strain 2.02 %, Temperature -40.0 °F | 50%RH; ISO 11403-1 -2 | |
| 110.15 MPa @Strain 2.08 %, Temperature -20.0 °C | 15976 psi @Strain 2.08 %, Temperature -4.00 °F | DAM; ISO 11403-1 -2 | |
| 121.44 MPa @Strain 3.10 %, Temperature -20.0 °C | 17613 psi @Strain 3.10 %, Temperature -4.00 °F | DAM; ISO 11403-1 -2 | |
| 122.61 MPa @Strain 2.54 %, Temperature -40.0 °C | 17783 psi @Strain 2.54 %, Temperature -40.0 °F | DAM; ISO 11403-1 -2 | |
| 124.84 MPa @Strain 3.61 %, Temperature -40.0 °C | 18107 psi @Strain 3.61 %, Temperature -40.0 °F | 50%RH; ISO 11403-1 -2 | |
| 133.68 MPa @Strain 3.33 %, Temperature -40.0 °C | 19389 psi @Strain 3.33 %, Temperature -40.0 °F | DAM; ISO 11403-1 -2 | |
| 138.48 MPa @Strain 4.29 %, Temperature -40.0 °C | 20085 psi @Strain 4.29 %, Temperature -40.0 °F | DAM; ISO 11403-1 -2 | |
| 5.00 MPa @Strain 0.370 %, Time 3600 sec | 725 psi @Strain 0.370 %, Time 1.00 hour | 50%RH; isochronous; ISO 11403-1 -2 | |
| 5.00 MPa @Strain 0.430 %, Time 36000 sec | 725 psi @Strain 0.430 %, Time 10.0 hour | 50%RH; isochronous; ISO 11403-1 -2 | |
| 5.00 MPa @Strain 0.490 %, Time 360000 sec | 725 psi @Strain 0.490 %, Time 100 hour | 50%RH; isochronous; ISO 11403-1 -2 | |
| 5.00 MPa @Strain 0.600 %, Time 3.60e+6 sec | 725 psi @Strain 0.600 %, Time 1000 hour | 50%RH; isochronous; ISO 11403-1 -2 | |
| 伸长率 (断裂) | 10 % | 10 % | DAM; ISO 527-1/-2 |
| 25 % | 25 % | 50%RH; ISO 527-1/-2 | |
| 拉伸模量 | 2.20 GPa | 319 ksi | 50%RH; ISO 527-1/-2 |
| 6.00 GPa | 870 ksi | DAM; ISO 527-1/-2 | |
| 0.936 GPa @Temperature 120 °C | 136 ksi @Temperature 248 °F | DAM; ISO 11403-1 -2 | |
| 4.911 GPa @Temperature 40.0 °C | 712.3 ksi @Temperature 104 °F | DAM; ISO 11403-1 -2 | |
| 8.087 GPa @Temperature -40.0 °C | 1173 ksi @Temperature -40.0 °F | DAM; ISO 11403-1 -2 | |
| 弯曲模量 | 5.90 GPa | 856 ksi | DAM; ISO 178 |
| 割线模量 | 0.401 GPa @Strain 15.19 %, Temperature 23.0 °C | 58.2 ksi @Strain 15.19 %, Temperature 73.4 °F | 50%RH; ISO 11403-1 -2 |
| 0.51614 GPa @Strain 11.4 %, Temperature 23.0 °C | 74.861 ksi @Strain 11.4 %, Temperature 73.4 °F | 50%RH; ISO 11403-1 -2 |